Categories | Carbon Fiber Profiles |
---|---|
Material:: | Polyacrylonitrile |
Category:: | Reinforced Composite Hard Felt |
Thermal conductivity:: | 0.15-0.25 |
Grade:: | A customized processing |
Refractory temperature:: | above 2000 ℃ |
Core material:: | polyacrylonitrile |
Form:: | Microporous |
Material thickness:: | 5-300mm |
Tube diameter:: | φ100-2500mm |
Tube wall thickness:: | 5-150mm |
Density:: | 0.18-0.32g.cm3 |
Place of Origin: | china |
Brand Name: | MTR |
Certification: | ISO CE |
MOQ: | Negotiation |
Price: | Negotiation |
Packaging Details: | Carton |
Delivery Time: | 15-20 working days or Negotiation |
Payment Terms: | T/T, L/C, D/P, West Union, Paypal, Secure Payments |
Supply Ability: | 100000 Kilogram/Kilograms per Year |
Reinforced Composite Hard Felt - Shaped Pieces
The Hunan MTR hard composite graphite felt is made of PAN (polyacrylonitrile) carbon fiber graphite felt through curing, carbonization and high temperature purification processing.
Physical and chemical indicators:
main material | PAN-CF / asphalt-CF / viscose-CF | Sheet specifications | length(mm) | 10-3000 |
Bulk density(g/CM3)) | 0.25-0.30 | width(mm) | 10-2000 | |
Thermal conductivity | 0.15-0.25(25℃)0.40-0.45(1400℃) | thickness(mm) | 5-300 | |
Barrel specifications | diameter(Φ) | Φ100-Φ2500 | ||
Carbon content(%) | ≧98 | Wall thickness(T) | 5-150 | |
bending strength(Gpa) | 1.8-3.5 | Tube height | 100-3000 | |
Flexural strength(Gpa) | 1.5-2.8 | Use environment | air(℃) | ≦350 |
ash content(ppm) | ≦300 | vacuum(℃) | ≦2200 | |
Processing temperature | First ≧1800 Second ≧2200 | Inert atmosphere(℃) | ≦3000 |
Temperature resistance: 2200 ℃ in vacuum, 3000 ℃ in inert gas
The density of this product is 0.18-0.35g/cm3. The surface can be coated with graphite paper or carbon cloth, carbon cloth and graphite paper, graphite paper can be sandwiched between each felt. It can prevent surface fluff, gas leakage (convection), and protect its surface (prevent loss) and increase the strength of hard felt.